The dissolution of simulant UK Ca/Zn-modified nuclear waste glass: the effect of increased waste loading
- 18 February 2021
- journal article
- research article
- Published by Springer Science and Business Media LLC in MRS Advances
- Vol. 6 (4-5), 95-102
- https://doi.org/10.1557/s43580-021-00025-0
Abstract
The influence of increasing the waste loading of Ca- and Zn-containing MW high-level-waste glass, from 20 to 35 wt%, on the chemical durability was investigated using 112-day PCT-B tests at 90 °C in ultra-high-quality water. During the initial stage of dissolution, from 0 to 3 days, increased waste loadings corresponded to reduced boron dissolution rates. By 112 days, however, there was no difference in the normalised mass loss of boron as a function of waste loading, within experimental uncertainty. In comparison to literature values obtained for traditional MW high-level-waste glasses, containing no Ca and Zn, the boron dissolution rates of CaZn MW glasses in the residual stage of dissolution, > 28 days, were greater by at least an order of magnitude. Analysis of secondary phases, combined with geochemical modelling of the solutions, indicate that the dual formation of Mg- and Zn-smectite phyllosilicate clays, potentially saponite (Ca0.2Mg3(Si,Al)4O10(OH)2·4H2O) and sauconite (Na0.3Zn3(Si, Al)4O10(OH)2·nH2O), respectively, may be the cause of this enhanced dissolution. Graphic abstractKeywords
Funding Information
- Engineering and Physical Sciences Research Council (EP/N017374/1, EP/L015390/1)
This publication has 27 references indexed in Scilit:
- Short communication: The dissolution of UK simulant vitrified high-level-waste in groundwater solutionsJournal of Nuclear Materials, 2020
- Chemical durability of UK vitrified high level waste in Si-saturated solutionsMaterials Letters, 2018
- The influence of ZnO incorporation on the aqueous leaching characteristics of a borosilicate glassJournal of Nuclear Materials, 2017
- Alteration layer formation of Ca- and Zn-oxide bearing alkali borosilicate glasses for immobilisation of UK high level waste: A vapour hydration studyJournal of Nuclear Materials, 2016
- Effect of Zn- and Ca-oxides on the structure and chemical durability of simulant alkali borosilicate glasses for immobilisation of UK high level wastesJournal of Nuclear Materials, 2015
- Phase Separation and Crystallisation in UK HLW Vitrified ProductsProcedia Materials Science, 2014
- Current Understanding and Remaining Challenges in Modeling Long‐Term Degradation of Borosilicate Nuclear Waste GlassesInternational Journal of Applied Glass Science, 2013
- New Insight into the Residual Rate of Borosilicate Glasses: Effect of S/V and Glass CompositionInternational Journal of Applied Glass Science, 2013
- An international initiative on long-term behavior of high-level nuclear waste glassMaterials Today, 2013
- SON68 nuclear glass dissolution kinetics: Current state of knowledge and basis of the new GRAAL modelJournal of Nuclear Materials, 2008