Experimental Study on Thermosensitive Hydrogel Used to Extinguish Class A Fire
Open Access
- 24 January 2021
- Vol. 13 (3), 367
- https://doi.org/10.3390/polym13030367
Abstract
Hydrogels are crosslinked polymers that become fully swollen when placed in aqueous environments. They are widely used in the field of firefighting because they can remarkably increase the viscosity and wettability of water. In this study, a thermosensitive hydrogel used to effectively suppress class A fire was synthesized by using methylcellulose, sodium polyacrylate, and magnesium chloride. The structure, surface activity and viscosity of the hydrogel were characterized. Fire extinguishing performance was evaluated based on small-scale and large-scale experiments. The results showed that a phase transition of the hydrogel occurred when the temperature rose from 50 °C to 80 °C. After the phase transition, the hydrogel showed a higher viscosity and lower surface tension, which was conducive to attach to the surface of the burning material and acting as an effective barrier to isolate oxygen. The small-scale fire extinguishing tests indicated that the concentration of the hydrogel solution has an eminent influence on fire extinguishing performance. The optimum concentration for extinguishing performance was around 6 wt%. The large-scale experiments demonstrated that the fire-extinguishing performance of this thermosensitive hydrogel was superior to the two other commercial water-based fire extinguishing agents, as it prevented re-ignition highly efficiently.This publication has 30 references indexed in Scilit:
- A description of the initial fire sprinkler sprayFire Safety Journal, 2016
- A study on the fire extinguishing characteristics of deep-seated fires using the scale model experimentFire Safety Journal, 2016
- Thermoresponsive hydrogels in biomedical applicationsEuropean Journal of Pharmaceutics and Biopharmaceutics, 2015
- Synthesis and characterization of a temperature‐sensitive hydrogel based on sodium alginate and N‐isopropylacrylamidePolymers for Advanced Technologies, 2015
- Mechanism and Property of Extinguishing Temperature-Sensitive HydrogelsPublished by Institute of Electrical and Electronics Engineers (IEEE) ,2014
- Thermo-sensitive chitosan–cellulose derivative hydrogels: swelling behaviour and morphologic studiesCellulose, 2014
- Comparative Performance of Three Magnesium Compounds on Thermal Degradation Behavior of Red Gum WoodMaterials, 2014
- Experimental study of the downward displacement of fire-induced smoke by water spraysFire Safety Journal, 2013
- Influence of neutral inorganic chlorides on primary and secondary char formation from celluloseJournal of Wood Science, 2008
- In situ-forming hydrogels—review of temperature-sensitive systemsEuropean Journal of Pharmaceutics and Biopharmaceutics, 2004