In this study epoxy phenol novalac resin which consists of silica nanoparticles and unsaturated poly ester resin linked to the Silane and cross linking to that structure and also parameters affecting the processes involved have been evaluated. Cross linking in phenol novalac epoxy resins effects on many properties such as thermal, electrical, mechanical and chemical attributes especially in elevated temperatures. Silane cross-linking’s in phenol novalac epoxy resin with respect to other methods like proxiding, irradiation and utilization of Azo compounds, looks to be a very simple and low cost route, which makes it very encouraging for various industries. Unsaturated poly ester resin is compatible with phenol novalac epoxy resin and also creates some cross-linking and as far as tri methoxy Silane is added to the mentioned resin, its thermal, physical and mechanical properties are optimized. In this literature impact, tension, glass transition temperature, humidity absorption, FTIR and Scanning electron microscopy (SEM) tests were done and the results revealed that as the cross-linking occurs, tension in rupture region increases. This increase is more common at elevated temperatures. The growth in content of silica nanoparticles leads to a drop in water permeability of phenol novalac epoxy resin nanocomposite which contains unsaturated poly ester resin.