Selective Polishing of Amorphous Silicon Carbonitride (a-SiCN) Films Over Silicon Dioxide and Silicon Nitride Films for Hardmask Applications
- 3 March 2020
- journal article
- research article
- Published by The Electrochemical Society in ECS Journal of Solid State Science and Technology
- Vol. 9 (3), 034004
- https://doi.org/10.1149/2162-8777/ab7b45
Abstract
We show that several amino acids and taurine, an aminosulfonic acid, when used as additives in 1 wt% silica slurries enhance a-SiCN removal rates (RRs) in the pH range 3-9. High RRs of 120 nm min(-1) and 160 nm min(-1) were obtained with 0.13 M glycine + 1 wt% silica at pH 5 and with 0.13 M taurine + 1 wt% silica at pH 6, respectively, both at an applied pressure of 3 psi. These compositions suppressed silicon nitride and silicon dioxide RRs to < 2 nm min(-1), making them excellent candidates for polishing a-SiCN hard mask layers during semiconductor fabrication. The role of the amino acids and taurine in polishing a-SiCN films was investigated using zeta potential measurements, attenuated total reflection-Fourier transform infrared (ATR-FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS). The reactivity of the deprotonated carboxyl species of the amino acids with SiCN surface is responsible for the observed rate enhancement while the binding of the protonated amine species of the amino acids with the silicon nitride surface suppresses nitride RRs at pH 5 and higher. The higher reactivity of taurine's sulfonic group is responsible for its higher polish rate. Oxide RR is low due to low silica particle loading of 1 wt%. (C) 2020 The Electrochemical Society ("ECS"). Published on behalf of ECS by IOP Publishing Limited.Keywords
Funding Information
- Intel Corporation
This publication has 34 references indexed in Scilit:
- Influence of Composition of SiCN as Interfacial Layer on Plasma Activated Direct BondingECS Journal of Solid State Science and Technology, 2019
- Study on the Polishing Performance of Silicon Carbonitride (SiCN)ECS Transactions, 2016
- Shallow Trench Isolation Chemical Mechanical Planarization: A ReviewECS Journal of Solid State Science and Technology, 2015
- Characterization of SiCN thin films: Experimental and theoretical investigationsThin Solid Films, 2014
- Effect of Transition Metal Compounds on Amorphous SiC Removal RatesECS Journal of Solid State Science and Technology, 2014
- Role of ionic strength in chemical mechanical polishing of silicon carbide using silica slurriesColloids and Surfaces A: Physicochemical and Engineering Aspects, 2014
- Atmospheric-Pressure Plasma-Enhanced Chemical Vapor Deposition of a-SiCN:H Films: Role of Precursors on the Film Growth and PropertiesACS Applied Materials & Interfaces, 2012
- Structural analysis of silicon carbon nitride films prepared by vapor transport-chemical vapor depositionJournal of Applied Physics, 2010
- Surfactants in Controlling Removal Rates and Selectivity in Barrier Slurry for Cu CMPMRS Proceedings, 2007
- Interfacial Reactivity Between Ceria and Silicon Dioxide and Silicon Nitride SurfacesElectrochemical and Solid-State Letters, 2005