Effects of calcium formate on early-age strength and microstructure of high-volume fly ash cement systems
- 1 December 2021
- journal article
- research article
- Published by Thomas Telford Ltd. in Magazine of Concrete Research
- Vol. 73 (24), 1283-1295
- https://doi.org/10.1680/jmacr.20.00118
Abstract
Fly ash (FA) is used as supplementary cementitious material to Ordinary Portland cement (PC) to reduce environmental impact and improve long-term properties of concrete. However, the replacement level of PC by FA is currently limited to 15%-30% in the industry, mainly due to problems with early age strength development. This research used calcium formate (CF) as an admixture in high volume fly ash (HVFA) composites to find the optimal dosages of CF that improve the early age strength most. From very low dosage of 0.5%, up to high dosage of 9% of CF were tried on PC and HVFA pastes with 60% and 70% FA. Compressive strength testing was performed as a preliminary identification of optimal mix designs to give the highest strength. Isothermal calorimetry, thermogravimetric analysis (TGA), x-ray diffraction (XRD) and scanning electron microscopy (SEM) were conducted to further investigate the effects of CF regarding hydration and microstructural aspects. The results show that PC pastes reached the highest strength with 2% CF. Both HVFA pastes with 60% and 70% FA achieved the highest strength at the CF dosage of 3%. At the age of 28 days, adding of 3% CF in HVFA mixes lead to more consumption of FA as well as more formation of CH, C-S-H, CaCO3 and ettringite which contribute to the increase of strength. Adding of very high CF dosage at 9% increased the hydration of C3A but could hinder the hydration of C3S in both PC and HVFA pastes with 60% and 70% FA.Keywords
This publication has 23 references indexed in Scilit:
- Early-age strength development in fly ash blended cement composites: investigation through chemical activationMagazine of Concrete Research, 2019
- Workability and mechanical properties of alkali-activated fly ash-slag concrete cured at ambient temperatureConstruction and Building Materials, 2018
- Hydration development of mineral additives blended cement using thermogravimetric analysis (TGA): Methodology of calculating the degree of hydrationConstruction and Building Materials, 2017
- Use of gypsum and CKD to enhance early age strength of High Volume Fly Ash (HVFA) pastesConstruction and Building Materials, 2014
- Binding mechanism and properties of alkali-activated fly ash/slag mortarsConstruction and Building Materials, 2013
- A review on the utilization of fly ashProgress in Energy and Combustion Science, 2010
- Industrially interesting approaches to “low-CO2” cementsCement and Concrete Research, 2004
- Effect of calcium formate as an accelerator on the physicochemical and mechanical properties of pozzolanic cement pastesCement and Concrete Research, 2004
- High Volume Fly Ash Abrasion Resistant ConcreteJournal of Materials in Civil Engineering, 2002
- Hydration versus strength in a portland cement developed from domestic mineral wastes — a comparative studyThermochimica Acta, 1986