Osteochondral repair using scaffolds with gradient pore sizes constructed with silk fibroin, chitosan, and nano-hydroxyapatite
Open Access
- 1 March 2019
- journal article
- research article
- Published by Taylor & Francis Ltd in International Journal of Nanomedicine
- Vol. ume 14, 2011-2027
- https://doi.org/10.2147/ijn.s191627
Abstract
Background: One of the main problems associated with the development of osteochondral reparative materials is that the accurate imitation of the structure of the natural osteochondral tissue and fabrication of a suitable scaffold material for osteochondral repair are difficult. The long-term outcomes of single- or bilayered scaffolds are often unsatisfactory because of the absence of a progressive osteochondral structure. Therefore, only scaffolds with gradient pore sizes are suitable for osteochondral repair to achieve better proliferation and differentiation of the stem cells into osteochondral tissues to complete the repair of defects. Methods: A silk fibroin (SF) solution, chitosan (CS) solution, and nano-hydroxyapatite (nHA) suspension were mixed at the same weight fraction to obtain osteochondral scaffolds with gradient pore diameters by centrifugation, freeze-drying, and chemical cross-linking. Results: The scaffolds prepared in this study are confirmed to have a progressive structure starting from the cartilage layer to bone layer, similar to that of the normal osteochondral tissues. The prepared scaffolds are cylindrical in shape and have high internal porosity. The structure consists of regular and highly interconnected pores with a progressively increasing pore distribution as well as a progressively changing pore diameter. The scaffold strongly absorbs water, and has a suitable degradation rate, sufficient space for cell growth and proliferation, and good resistance to compression. Thus, the scaffold can provide sufficient nutrients and space for cell growth, proliferation, and migration. Further, bone marrow mesenchymal stem cells seeded onto the scaffold closely attach to the scaffold and stably grow and proliferate, indicating that the scaffold has good biocompatibility with no cytotoxicity. Conclusion: In brief, the physical properties and biocompatibility of our scaffolds fully comply with the requirements of scaffold materials required for osteochondral tissue engineering, and they are expected to become a new type of scaffolds with gradient pore sizes for osteochondral repair.Keywords
This publication has 55 references indexed in Scilit:
- Effect of processing on silk‐based biomaterials: Reproducibility and biocompatibilityJournal of Biomedical Materials Research Part B: Applied Biomaterials, 2011
- Novel Nano-composite Multilayered Biomaterial for Osteochondral RegenerationThe American Journal of Sports Medicine, 2011
- Composite materials based on silk proteinsProgress in Polymer Science, 2010
- Emerging Techniques in Stratified Designs and Continuous Gradients for Tissue Engineering of InterfacesAnnals of Biomedical Engineering, 2010
- Arthroscopic Autologous Osteochondral Grafting for Cartilage Defects of the KneeThe American Journal of Sports Medicine, 2007
- Biomechanical properties of carbodiimide crosslinked collagen: Influence of the formation of ester crosslinksJournal of Biomedical Materials Research Part A, 2007
- Repair of Osteochondral Defects with Autologous Chondrocytes Seeded onto Bioceramic Scaffold in SheepTissue Engineering, 2004
- Tissue-Engineered Fabrication of an Osteochondral Composite Graft Using Rat Bone Marrow-Derived Mesenchymal Stem CellsTissue Engineering, 2001
- Tissue engineering of biphasic joint cartilage transplantsBiomaterials, 1999
- The apparent elastic modulus of the juxtaricular subchondral bone of the femoral headJournal of Orthopaedic Research, 1984