Switchable Catalysis Improves the Properties of CO2-Derived Polymers: Poly(cyclohexene carbonate-b-ε-decalactone-b-cyclohexene carbonate) Adhesives, Elastomers, and Toughened Plastics
Top Cited Papers
Open Access
- 20 February 2020
- journal article
- research article
- Published by American Chemical Society (ACS) in Journal of the American Chemical Society
- Vol. 142 (9), 4367-4378
- https://doi.org/10.1021/jacs.9b13106
Abstract
Carbon dioxide/epoxide copolymerization is an efficient way to add value to waste CO2 and to reduce pollution in polymer manufacturing. Using this process to make low molar mass polycarbonate polyols is a commercially relevant route to new thermosets and polyurethanes. In contrast, high molar mass polycarbonates, produced from CO2, generally under-deliver in terms of properties, and one of the most widely investigated, poly(cyclohexene carbonate), is limited by its low elongation at break and high brittleness. Here, a new catalytic polymerization process is reported that selectively and efficiently yields degradable ABA-block polymers, incorporating 6–23 wt % CO2. The polymers are synthesized using a new, highly active organometallic heterodinuclear Zn(II)/Mg(II) catalyst applied in a one-pot procedure together with biobased ε-decalactone, cyclohexene oxide, and carbon dioxide to make a series of poly(cyclohexene carbonate-b-decalactone-b-cyclohexene carbonate) [PCHC-PDL-PCHC]. The process is highly selective (CO2 selectivity >99% of theoretical value), allows for high monomer conversions (>90%), and yields polymers with predictable compositions, molar mass (from 38–71 kg mol–1), and forms dihydroxyl telechelic chains. These new materials improve upon the properties of poly(cyclohexene carbonate) and, specifically, they show good thermal stability (Td,5 ∼ 280 °C), high toughness (112 MJ m–3), and very high elongation at break (>900%). Materials properties are improved by precisely controlling both the quantity and location of carbon dioxide in the polymer chain. Preliminary studies show that polymers are stable in aqueous environments at room temperature over months, but they are rapidly degraded upon gentle heating in an acidic environment (60 °C, toluene, p-toluene sulfonic acid). The process is likely generally applicable to many other lactones, lactides, anhydrides, epoxides, and heterocumulenes and sets the scene for a host of new applications for CO2-derived polymers.Keywords
Funding Information
- Engineering and Physical Sciences Research Council (EP/K014668/1, EP/L017393/1, EP/S018603/1)
This publication has 82 references indexed in Scilit:
- Experimental and Computational Investigation of the Mechanism of Carbon Dioxide/Cyclohexene Oxide Copolymerization Using a Dizinc CatalystMacromolecules, 2012
- Triblock copolymers from lactide and telechelic poly(cyclohexene carbonate)Polymer Chemistry, 2012
- Preparation of thermoplastic polyurethanes using in situ generated poly(propylene carbonate)-diolsPolymer Chemistry, 2012
- Tailored Living Block Copolymerization: Multiblock Poly(cyclohexene carbonate)s with Sequence ControlMacromolecules, 2011
- Pressure-Sensitive Adhesives from Renewable Triblock CopolymersMacromolecules, 2010
- Immortal CO2/Propylene Oxide Copolymerization: Precise Control of Molecular Weight and Architecture of Various Block CopolymersMacromolecules, 2010
- Synthesis and physical characterization of poly(cyclohexane carbonate), synthesized from CO2 and cyclohexene oxidePolymer, 2001
- Viscoelastic Windows of Pressure-Sensitive AdhesivesThe Journal of Adhesion, 1991
- Poly(styrene-b-butadiene-b-4-vinylpyridine) Three-Block Polymers. Synthesis, Characterization, Morphology, and Mechanical PropertiesMacromolecules, 1980
- Structural Change Accompanied by Plastic-to-Rubber Transition of SBS Block CopolymersRubber Chemistry and Technology, 1978