Role of copper in the green luminescence from ZnO crystals

Abstract

Electron paramagnetic resonance(EPR),photoluminescence, and infrared optical absorption have been used to investigate a ZnO crystal before and after a thermal anneal for 1 h in air at 900 °C. The sample was an undoped high quality crystal grown by the chemical vapor transport method. In addition to shallow donor impurities, the crystal contained trace amounts of copper ions. Prior to the thermal anneal, these ions were all in the Cu + (3d 10 ) state and the observed luminescence at 5 K, produced by 364 nm light, consisted of a broad structureless band peaking at 500 nm. After the high-temperature anneal, the Cu 2+ (3d 9 ) EPRspectrum was observed and the luminescence had changed significantly. The emission then peaked near 510 nm and showed structure identical to that reported by Dingle [Phys. Rev. Lett. 23, 579 (1969)]. Our data reaffirm that the structured green emission in ZnO is associated with Cu 2+ ions. We suggest that the unstructured green emission (observed before the high-temperature anneal) is donor–acceptor pair recombination involving the Cu + acceptors.