Study of the Bimetallic Joint CuCrZr/316L(N)

Abstract

In this work, a study of the cases of destruction of the CuCrZr / 316L (N) bimetallic joint (BMJ) obtained by diffusion welding under conditions of hot isostatic pressing (HIP) was carried out. The identified defects are cracks propagating in the BMJ zone in the corner zone of the mock-ups of the heat-sink elements (HE). The analysis of the causes of destruction of the BMJ was carried out and the factors leading to the weakening of the BMJ zone are analyzed. The analysis of the thermal and stress-strain state of the HE mock-up during the manufacturing process was carried out. The study of the elements of the HE mock-up were carried out by methods of non-destructive testing (ultrasonic testing (UT)) and destructive testing (metallography; fractography; energy-dispersive X-ray spectroscopy; tensile tests). The inclusion of brittle phases in the zone of the BMJ was revealed and an assumption was made about the chemical composition of these phases. It was revealed that this line of brittle phases is a crack propagation zone in all cases of destruction of the BMJ in the HE mock-ups. The temperature range is revealed at which the effect of "ductility failure" of the CuCrZr is observed during the tensile testing of the samples.