Fatigue Life of Green Stabilized Fiber-Reinforced Sulfate-Rich Dispersive Soil
- 1 September 2021
- journal article
- research article
- Published by American Society of Civil Engineers (ASCE) in Journal of Materials in Civil Engineering
- Vol. 33 (9), 04021249
- https://doi.org/10.1061/(asce)mt.1943-5533.0003842
Abstract
Sulfate-rich dispersive soils are worldwide responsible for damaging earthworks, such as roadway roadbeds and embankments. One of the causes for such behavior is the high amount of exchangeable sodium ions adsorbed on their clay particles vastly increasing erosion susceptibility, being responsible for problems as piping, ravines, and water turbidity. In order to reduce the erodibility, it is usual to treat such soils with calcium-based stabilizers. However, in the presence of sulfates, when combined with calcium-based stabilizers in the soil, reactions take place between stabilizers and sulfates to form expansive minerals. Namely, these minerals are known as ettringite and thaumasite and are responsible for excessive volumetric swell. In this context, the present research aims to develop alternative soil stabilizers (industrial byproducts plus artificial pozzolans) and reinforcements (fiberglass) to solve problems associated with sulfate-rich dispersive soils. Thus, a binder composed of carbide lime and ground glass was used. In addition, fiberglass was applied to look for enhanced mechanical properties of the materials. To assess the efficiency of the proposed stabilization and reinforcement, unconfined compressive and splitting tensile strength, ultrasonic pulse velocity, wet and dry durability, and fatigue life tests were carried out. Soil–ground glass–carbide lime-fiberglass blends were molded at different porosities, carbide lime, ground glass, and fiberglass contents. Results show that unconfined compressive and split tensile strength and initial shear modulus are highly dependent on changes in porosity and lime content. Durability, expressed as the accumulated loss of mass, could be assessed through the adjusted porosity/lime index ( ). Fiberglass inclusion resulted in higher tensile strength. The fatigue life was correlated to the index through a negative exponent. The greater the carbide lime level, the smaller was the fatigue life for all treated specimens. An increase in porosity results in fewer contacts between particles, whereas an increase in carbide lime content enhanced the specimen’s rigidity.
Keywords
This publication has 40 references indexed in Scilit:
- Key parameters dictating strength of lime/cement-treated soilsGeotechnical Engineering, 2009
- Factors Affecting Spontaneous Dispersion of soil Materials as Evidenced by the Crumb TestPublished by ASTM International ,2009
- Some Engineering Problems with Dispersive ClaysPublished by ASTM International ,2009
- Performance of a fibre-reinforced sand at large shear strainsGéotechnique, 2007
- Hydrated Lime Stabilization of Sulfate-Bearing Vertisols in TexasTransportation Research Record: Journal of the Transportation Research Board, 2004
- Experimental evaluations of stabilisation methods for sulphate-rich expansive soilsProceedings of the Institution of Civil Engineers - Ground Improvement, 2003
- Effects of Fiber Reinforcement on Strength and Volume Change in Expansive SoilsTransportation Research Record: Journal of the Transportation Research Board, 2000
- LIME MODIFICATION OF CLAY SOILS FOR CONSTRUCTION EXPEDIENCY.Geotechnical Engineering, 1997
- Ettringite-Induced Swelling in Soils: State-of-the-ArtApplied Mechanics Reviews, 1995
- Preparing Test Specimens Using UndercompactionGeotechnical Testing Journal, 1978