Systematic Structural and Optical Characterization of TiO2 Nanofibres Synthesised by Electrospinning
- 24 September 2021
- journal article
- Published by World Scientific and Engineering Academy and Society (WSEAS) in WSEAS TRANSACTIONS ON ELECTRONICS
- Vol. 12, 106-115
- https://doi.org/10.37394/232017.2021.12.15
Abstract
TiO2 nanofibres were synthesised by means of the electrospinning technique, which were annealed at high temperatures to achieve the crystalline phase transformation. The chemical stoichiometry of electrospun TiO2 nanofibres was estimated by EDS, finding that at low annealing temperatures excess of oxygen was detected and at high temperatures excess of titanium that originates oxygen vacancies. TEM images show clearly the formation of TiO2 nanofibres that exhibit a homogeneous and continuous aspect without the presence of crystalline defects, whose surface morphology depends strongly on the annealing temperature. The crystalline phase transformation was studied by Raman spectroscopy, which revealed that annealed TiO2 nanofibres showed a crystalline phase transformation from pure anatase to, first a mix of anatase-rutile, then pure rutile as the annealing temperature increased, which was corroborated by X-ray diffraction and high-resolution TEM microscopy. The average grain size, inside the nanofibres, increased with the crystalline phase transformation from 10 to 24 nm for anatase-TiO2 and from 30 to 47 nm for rutile-TiO2, estimated by using the Scherrer-Debye equation. The band gap energy (Eg), obtained from optical absorption spectra, decreases monotonically, where a local minimum is observed at 700 °C, which is ranged in 3.75 Eg 2.42 eV, caused by the anatase → rutile crystalline phase transformation. The photoluminescence shows that radiative bands present a gradual red-shift as the annealing temperature increases due to the continuous change of Eg.Keywords
This publication has 46 references indexed in Scilit:
- Raman spectra of titanium dioxide (anatase, rutile) with identified oxygen isotopes (16, 17, 18)Physical Chemistry Chemical Physics, 2012
- Photocatalytic degradation of Rhodamine B dye under UV/solar light using ZnO nanopowder synthesized by solution combustion routePowder Technology, 2012
- Dumbbell shaped nickel nanocrystals synthesized by a laser induced fragmentation methodJournal of Materials Chemistry, 2011
- A Novel Mixed Reverse Microemulsion Route for the Synthesis of Nanosized Titania Particles~!2009-01-28~!2010-06-04~!2010-08-13~!The Open Mineral Processing Journal, 2010
- Chemistry and Properties of Nanocrystals of Different ShapesChemical Reviews, 2005
- A review on polymer nanofibers by electrospinning and their applications in nanocompositesComposites Science and Technology, 2003
- Polymer nanofibers assembled by electrospinningCurrent Opinion in Colloid & Interface Science, 2003
- Recent Developments in PhotocatalysisDevelopments in Chemical Engineering and Mineral Processing, 1998
- Nanometre diameter fibres of polymer, produced by electrospinningNanotechnology, 1996
- Perspectives on the Physical Chemistry of Semiconductor NanocrystalsThe Journal of Physical Chemistry, 1996