Dilatometric investigations of Fe – Cr – Mo – C system
Open Access
- 21 December 2018
- journal article
- Published by Technical University of Varna in ANNUAL JOURNAL OF TECHNICAL UNIVERSITY OF VARNA, BULGARIA
- Vol. 2 (2), 1-13
- https://doi.org/10.29114/ajtuv.vol2.iss2.79
Abstract
Sintering behavior in high purity nitrogen and mixture of 5% H2-95% N2 of Fe-(Cr)-(Mo)-C system was investigated. The mixtures, differ from chromium, molybdenum and carbon content were prepared in Turbula mixer. Then, using single-action pressing in a rigid die at pressing pressure 400 MPa, green compacts with density level 5.9±0.17 g/cm3 were pressed. Sintering was carried out in a horizontal push rod dilatometer Netzsch 402E at 1120 and 1250°C for 60 min. Heating and cooling rates were 10 and 20°C/min., respectively. After heating, compacts were isothermal sintered at 1120 or 1250°C for 60 minutes an cooled up to 200°C, then isothermally hold for 60 minutes and definitely cooled to the room temperature. Pure nitrogen and mixture of 5% H2-95% N2 were employed as sintering atmospheres. During investigations the influence of isothermal sintering temperature, chemical composition of sintering atmosphere, chromium, molybdenum and carbon content was followed by dilatometry. The aim of investigations was to determine transformation temperatures. It was shown that the dimensional changes occurring during heating and isothermal sintering and the final density of sintered compacts are influenced by sintering parameters and the alloying elements concentration in powder mixture.Keywords
This publication has 6 references indexed in Scilit:
- Effect of local sintering microatmosphere on mechanical properties of Fe–3Cr–0·5Mo–0·6C steelPowder Metallurgy, 2013
- Characterization of Wear Mechanisms in Sintered Fe-1.5 Wt % Cu AlloysArchives of Metallurgy and Materials, 2012
- Manganese in Powder Metallurgy SteelsPublished by Springer Science and Business Media LLC ,2012
- Microstructure and Mechanical Properties of Cr-Mn Structural PM SteelsArchives of Metallurgy and Materials, 2011
- Tensile properties of Fe-3Mn-0·6/0·7C steels sinteredin semiclosed containers in dry hydrogen, nitrogen and mixtures thereofPowder Metallurgy, 2003
- EFFECT OF ADDITIONAL ALLOYING ELEMENTS ON THE PROPERTIES OF SINTERED MANGANESE STEELSPowder Metallurgy, 1975