In situ formation of zinc oxide on bamboo bleached pulp in preparation of antibacterial paper: Effect of precursors addition

Abstract

An approach of green in situ synthesis single-step method was applied to produce antibacterial paper. The objective was to investigate the effect of precursor addition on the formation of zinc oxide particles using an in situ single-step method. Zinc chloride concentrations of 0.1, 0.3, 0.5, and 0.7 M were prepared and added into a solution of algae extract and bamboo pulp. The prepared pulps were tested and made into handsheets using a papermaking machine based on TAPPI T205 (2006). Morphological observation of treated papers was conducted using a field emission scanning electron microscope (FESEM). An average of 400 to 570 nm zinc oxide spherical-shaped particle was observed on the fibers of paper. The percentage of element composition of the treated paper were 15.08% to 34.08% of zinc and 17.45% to 32.59% of oxygen captured via scanning electron microscopy with energy dispersive X-ray (SEM-EDX) analysis. The crystallinity test was performed using X-ray dispersion (XRD). A higher percentage of precursors exhibited a more amorphous structure. A measurement of more than 30% increment of inhibition zone was obtained from 10.00 to 25.00 mm against S. aureus, S. choleraesuis, and E. coli. Precursors addition of more than 0.3 M would have the most potential to enhance the growth of zinc oxide via in situ preparation, hence providing better antibacterial properties of the prepared papers.