Phase transformation behaviors and mechanical properties of NiTi endodontic files after gold heat treatment and blue heat treatment
- 1 January 2021
- journal article
- research article
- Published by Nihon University School of Dentistry in Journal of Oral Science
- Vol. 63 (1), 8-13
- https://doi.org/10.2334/josnusd.19-0331
Abstract
WaveOne Gold, ProTaper Gold, Reciproc Blue, ProTaper Next, WaveOne and ProTaper files were selected to compare the phase transformation behaviors and mechanical properties of nickel-titanium (NiTi) rotary files after gold heat and blue heat treatments. The reverse transformation finishing point temperatures of WaveOne Gold, ProTaper Gold, ProTaper Next and WaveOne were higher than those of the other two instruments investigated. At a deflection of 0.5 mm, the loads were significantly varied except for ProTaper Next and ProTaper Gold. At a deflection of 3.0 mm, the loads of Reciproc Blue and WaveOne Gold were significantly varied compared to WaveOne and ProTaper. Cycles to failure were reduced in the order of WaveOne Gold, Reciproc Blue, ProTaper Gold, ProTaper Next, WaveOne and ProTaper. NiTi instruments after gold heat and blue heat treatments exhibited significantly higher bending properties and cyclic fatigue resistances, representing an improved performance over traditional and M-wire instruments.Keywords
This publication has 39 references indexed in Scilit:
- Evolution of nickel–titanium instruments: from past to futureEndodontic Topics, 2013
- Fatigue resistance of rotary instruments manufactured using different nickel–titanium alloys: a comparative studyOdontology, 2012
- Phase transformation behaviour and bending property of twisted nickel-titanium endodontic instrumentsInternational Endodontic Journal, 2011
- Low-cycle fatigue life of superelastic NiTi wiresInternational Journal of Fatigue, 2009
- Mechanical properties of a new and improved nickel-titanium alloy for endodontic use: an evaluation of file flexibilityOral Surgery, Oral Medicine, Oral Pathology, Oral Radiology, and Endodontology, 2008
- Influence of phase transformation on the torsional and bending properties of nickel–titanium rotary endodontic instrumentsInternational Endodontic Journal, 2006
- Thermal processing of polycrystalline NiTi shape memory alloysMaterials Science and Engineering: A, 2005
- Physical metallurgy of Ti–Ni-based shape memory alloysProgress in Materials Science, 2005
- Fatigue-crack growth behavior in the superelastic and shape-memory alloy nitinolMetallurgical and Materials Transactions, 2001
- A study of electrical resistivity, internal friction and shear modulus on an aged Ti49Ni51 alloyActa Metallurgica et Materialia, 1990