The different effects of preheating and heat treatment on the surface microhardness of nanohybrid resin composite
Open Access
- 31 March 2020
- journal article
- Published by Universitas Airlangga in Dental Journal (Majalah Kedokteran Gigi)
- Vol. 53 (1), 6-9
- https://doi.org/10.20473/j.djmkg.v53.i1.p6-9
Abstract
Background: A composite resin is used as restorative material in dentistry because it has the same colour as dental enamel, is easy to use in an oral cavity and offers good biocompatibility. Based on the size of filler, composite resin is divided into types, one of which is a composite resin nanohybrid. An important mechanical property of restorative material is microhardness. The mechanical properties of restorative material is highly affected by both polymerisation and heating process. There are many methods to improve composite resin’s microhardness, including preheating and heat treatment. Purpose: The purpose of this study was to evaluate different effects of preheating and heat treatment on the microhardness of nanohybrid composite resin. Methods: This study is an experimental laboratory research with post-test-only group design. Samples were divided into six groups: preheating groups at temperatures of 37oC and 60oC, heat treatment groups at temperatures of 120oC and 170oC, a negative control group and a positive control group. Afterwards, the resulting data were analysed using one-way ANOVA. Results: The result based on the one-way ANOVA test indicated that there was a difference in microhardness in each group with a significance of 0.000 (pConclusion: The conclusion of this study was the best microhardness of composite resin nanohybrid is the heat treatment group at temperature 170oC.Keywords
This publication has 20 references indexed in Scilit:
- Pre-heating of high-viscosity bulk-fill resin composites: Effects on shrinkage force and monomer conversionJournal of Dentistry, 2015
- UJI KEKERASAN RESIN KOMPOSIT AKTIVASI SINAR DENGAN BERBAGAI JARAK PENYINARANe-GiGi, 2015
- PERBEDAAN PENGARUH HIDROGEN PEROKSIDA 35% DAN KARBAMID PEROKSIDA 35% TERHADAP MICROLEAKAGE PADA RESIN KOMPOSIT NANOHYBRIDODONTO : Dental Journal, 2015
- Effect of Heat Treatment on the Physical Properties of Provisional Crowns during Polymerization: An in Vitro StudyMaterials, 2015
- Effect of Nanofiller Technology on Surface Properties of Nanofilled and Nanohybrid CompositesInternational Journal of Dentistry and Oral Health, 2015
- Compressive strength resin komposit hybrid post curing dengan light emitting diode menggunakan tiga ukuran lightbox yang berbedaDental Journal (Majalah Kedokteran Gigi), 2013
- Influence of heat treatment on the sorption and solubility of direct composite resinsIndian Journal of Dental Research, 2013
- Effect of Precuring Warming on Mechanical Properties of Restorative CompositesInternational Journal of Dentistry, 2011
- Resin composite restorative materialsAustralian Dental Journal, 2011
- Heat treatment of a direct composite resin: influence on flexural strengthBrazilian Oral Research, 2009