REALIZATION OF MULTI-STAGE MODEL OF BABBIT FATIGUE DAMAGES AND BABBIT ANTI-FRICTION LAYERS
- 9 March 2021
- journal article
- Published by Bryansk State Technical University BSTU in Bulletin of Bryansk state technical university
- Vol. 2021 (3)
- https://doi.org/10.30987/1999-8775-2021-3-4-15
Abstract
The research purpose is to realize a multi-stage model developed by the authors to show fatigue failures accumulation and failures of anti-friction materials and layers in slider bearings. The model describes: a scattered accumulation of micro-cracks, formation and development of a micro-crack system up to a limiting state of an object. There are solved some problems. The problem of model parameter identification on the basis of the analysis of babbit sample tests is solved with the use of the simplest optimization method – a method of a deformable polyhedron. At that there are used principles of the least-squares method. A new result is four model parameters obtained finally. A computation problem of anti-friction babbit layer life required the development of a new software product. Software testing is carried out as a comparison of bearing-sample tested for fatigue and calculated life of these samples. The calculated and experimental lives are consistent. It confirms model working capacity.Keywords
This publication has 7 references indexed in Scilit:
- APPLICABILITY ANALYSIS OF STRESS STATE CRITERIA FOR DESCRIPTION OF BABBIT LAYER FATIGUE DESTRUCTION IN SLIDER BEARINGSBulletin of Bryansk state technical university, 2019
- MODELS OF PHYSICALLY SHORT AND MACROSCOPIC CRACK DEVELOPMENT AND THEIR APPLICATION FOR TIN BASED BABBITBulletin of Bryansk state technical university, 2019
- EXPERIMENTAL AND COMPUTATION INVESTIGATIONS OF STRESS STATE IMPACT UPON BABBIT LAYER FATIGUE LIFE OF SLIDER BEARINGBulletin of Bryansk state technical university, 2018
- STATISTICAL PRINCIPLE FOR BOUNDARY DEFINITION IN DEVELOPMENT OF SHORT CRACKS INTO MACRO-CRACKS AND ITS REALIZATION FOR TIN-BASED BABBITBulletin of Bryansk state technical university, 2017
- STRESSED STATE IN ANTI-FRITICAL SLIDE BEARING WITH CRACKBulletin of Bryansk state technical university, 2017
- CRACK RESISTANCE OF BABBIT B83Bulletin of Bryansk state technical university, 2017
- Tests for equivalence of the stress state and the generalized stress-strain diagram babbitt Tin-based.Bulletin of Bryansk state technical university, 2014