In situ nanoindentation during electrochemical hydrogen charging: a comparison between front-side and a novel back-side charging approach
Open Access
- 27 January 2021
- journal article
- research article
- Published by Springer Science and Business Media LLC in Journal of Materials Science
- Vol. 56 (14), 8732-8744
- https://doi.org/10.1007/s10853-020-05749-2
Abstract
The effects of hydrogen in metals are a pressing issue causing severe economic losses due to material deterioration by hydrogen embrittlement. A crucial understanding of the interactions of hydrogen with different microstructure features can be reached by nanoindentation due to the small volumes probed. Even more, in situ testing while charging the sample with hydrogen prevents the formation of concentration gradients due to hydrogen desorption. Two custom electrochemical cells for in situ testing were built in-house to charge the sample with hydrogen during nanoindentation: “front-side” charging with the sample and the indenter tip immersed into the electrolyte, and “back-side” charging where the analyzed region is never in contact with the solution. During front-side charging, surface degradation often occurs which also negatively influences analyses after hydrogen charging. The back-side charging approach proposed in this work is a promising technique for studying in situ the effects of hydrogen in alloys under mechanical loads, while completely excluding the influence of the electrolyte on the nanoindented surface. Hydrogen diffusion from the charged back-side toward the testing surface is here demonstrated by Kelvin probe measurements in ferritic FeCr alloys, used as a case study due to the high mobility of hydrogen in the bcc lattice. During nanoindentation, a reduction on the shear stress necessary for dislocations nucleation due to hydrogen was observed using both setups; however, the quantitative data differs and a contradictory behavior was found in hardness measurements. Finally, some guidelines for the use of both approaches and a summary of their advantages and disadvantages are presented. Graphical abstractKeywords
Funding Information
- Deutsche Forschungsgemeinschaft (DU 1628/1-1)
- H2020 European Research Council (787446-GB-CORRELATE)
- Projekt DEAL
This publication has 43 references indexed in Scilit:
- Atomic mechanism and prediction of hydrogen embrittlement in ironNature Materials, 2012
- Hydrogen embrittlement phenomena and mechanismsCorrosion Reviews, 2012
- Hydrogen Absorption and Desorption in Steel by Electrolytic ChargingAdvanced Materials Research, 2006
- Transmission electron microscopy observations and micromechanical/continuum models for the effect of hydrogen on the mechanical behaviour of metalsPhilosophical Magazine A, 2002
- Transmission electron microscopy observations and micromechanical/continuum models for the effect of hydrogen on the mechanical behaviour of metalsPhilosophical Magazine A, 2002
- Nanomechanical probes as new approaches to hydrogen/deformation interaction studiesEngineering Fracture Mechanics, 2001
- The effect of hydrogen on dislocation dynamicsEngineering Fracture Mechanics, 1999
- Indentation induced dislocation nucleation: The initial yield pointActa Materialia, 1996
- Hydrogen-enhanced localized plasticity—a mechanism for hydrogen-related fractureMaterials Science and Engineering: A, 1994
- An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experimentsJournal of Materials Research, 1992