Inclusion Evolution in Al-Killed Ca-Treated Steels at Heat Treatment Temperature In Situ Observed Using Confocal Scanning Laser Microscope
- 6 March 2022
- journal article
- research article
- Published by Springer Science and Business Media LLC in Metallurgical and Materials Transactions B
- Vol. 53 (3), 1323-1328
- https://doi.org/10.1007/s11663-022-02472-y
Abstract
No abstract availableKeywords
This publication has 29 references indexed in Scilit:
- Calcium Modification of Spinel Inclusions in Aluminum-Killed Steel: Reaction StepsMetallurgical and Materials Transactions B, 2012
- Transient Inclusion Evolution During Modification of Alumina Inclusions by Calcium in Liquid Steel: Part I. Background, Experimental Techniques and Analysis MethodsMetallurgical and Materials Transactions B, 2011
- Composition change in oxide inclusions of stainless steel by heat treatmentIron and Steelmaking, 2010
- Control of MgO·Al2O3 Spinel Inclusions in Stainless SteelsISIJ International, 2010
- Aluminum Deoxidation Equilibrium of Molten Iron–Aluminum Alloy with Wide Aluminum Composition Range at 1 873 KISIJ International, 2009
- Aluminum Deoxidation Equilibrium of Molten Fe–Ni Alloy Coexisting with Alumina or HercyniteISIJ International, 2008
- State of the art in the control of inclusions during steel ingot castingMetallurgical and Materials Transactions B, 2006
- The Ability of Slags to Absorb Solid Oxide InclusionsISIJ International, 2006
- Dissolution Rate of Al2O3 into Molten CaO-SiO2-Al2O3 Slags.ISIJ International, 2002
- Reoxidation Behavior of Molten Steel in Tundish.ISIJ International, 2000